ASTM A789 stainless steel pipe
ASTM A789 S31803 Stainless Pipe
C | Mn | P | S | Si | Ni | Cr | Mo | N | other |
0.030 | 2.00 | 0.030 | 0.020 | 1.00 | 4.50-6.50 | 21.0-23.0 | 2.5-3.5 | 0.08-0.20 | - |
Yield Strength min, Ksi [Mpa] | Tensile Strength, min, Ksi [Mpa] | Elongation in 2 in. or in 50mm, min, % | Hardness, max | ||||||
HBW | HRC | ||||||||
65[450] | 90[620] | 25 | 290 | 30 |
ASTM A789 S32205 Stainless Pipe
C | Mn | P | S | Si | Ni | Cr | Mo | N | other |
0.030 | 2.00 | 0.030 | 0.020 | 1.00 | 4.50-6.50 | 21.0-23.0 | 3.0-3.5 | 0.14-0.20 | - |
Yield Strength min, Ksi [Mpa] | Tensile Strength, min, Ksi [Mpa] | Elongation in 2 in. or in 50mm, min, % | Hardness, max | ||||||
HBW | HRC | ||||||||
70[485] | 95[655] | 25 | 290 | 30 |
ASTM A789 S31500 Stainless Pipe
C | Mn | P | S | Si | Ni | Cr | Mo | N | other |
0.030 | 1.20-2.00 | 0.030 | 0.030 | 1.40-2.00 | 4.30-5.20 | 18.0-19.0 | 2.5-3.0 | 0.05-0.1 | - |
Yield Strength min, Ksi [Mpa] | Tensile Strength, min, Ksi [Mpa] | Elongation in 2 in. or in 50mm, min, % | Hardness, max | ||||||
HBW | HRC | ||||||||
64[440] | 92[630] | 30 | 290 | 30 |
ASTM A789 S31200 Stainless Pipe
C | Mn | P | S | Si | Ni | Cr | Mo | N | other |
0.030 | 2.00 | 0.045 | 0.030 | 1.00 | 5.50-6.50 | 24.0-26.0 | 1.2-2.0 | 0.14-0.20 | - |
Yield Strength min, Ksi [Mpa] | Tensile Strength, min, Ksi [Mpa] | Elongation in 2 in. or in 50mm, min, % | Hardness, max | ||||||
HBW | HRC | ||||||||
65[450] | 100[690] | 25 | 280 | - |
ASTM A789 S31260 Stainless Pipe
C | Mn | P | S | Si | Ni | Cr | Mo | N | Cu |
0.030 | 1.00 | 0.030 | 0.030 | 0.75 | 5.50-7.50 | 24.0-26.0 | 2.5-3.5 | 0.10-0.30 | 0.20-0.80 |
Yield Strength min, Ksi [Mpa] | Tensile Strength, min, Ksi [Mpa] | Elongation in 2 in. or in 50mm, min, % | Hardness, max | ||||||
HBW | HRC | ||||||||
65[450] | 100[690] | 25 | 290 | - |
ASTM A789 S32001 Stainless Pipe
C | Mn | P | S | Si | Ni | Cr | Mo | N | Cu |
0.030 | 4.00-6.00 | 0.040 | 0.030 | 1.00 | 1.0-3.0 | 19.5-21.5 | 0.60 | 0.05-0.17 | 1.00 |
Yield Strength min, Ksi [Mpa] | Tensile Strength, min, Ksi [Mpa] | Elongation in 2 in. or in 50mm, min, % | Hardness, max | ||||||
HBW | HRC | ||||||||
65[450] | 90[620] | 25 | 290 | 30 |
ASTM A789 S39274 Stainless Pipe
C | Mn | P | S | Si | Ni | Cr | Mo | N | Cu |
0.030 | 1.00 | 0.030 | 0.020 | 0.80 | 6.0-8.0 | 24.0-26.0 | 2.5-3.5 | 0.24-0.32 | 0.20-0.80 |
Yield Strength min, Ksi [Mpa] | Tensile Strength, min, Ksi [Mpa] | Elongation in 2 in. or in 50mm, min, % | Hardness, max | ||||||
HBW | HRC | ||||||||
80[550] | 116[800] | 15 | 310 | 32 |
ASTM A789 S32750 Stainless Pipe
C | Mn | P | S | Si | Ni | Cr | Mo | N | Cu |
0.030 | 1.20 | 0.035 | 0.020 | 0.80 | 6.0-8.0 | 24.0-26.0 | 3.0-5.0 | 0.24-0.32 | 0.50 |
Yield Strength min, Ksi [Mpa] | Tensile Strength, min, Ksi [Mpa] | Elongation in 2 in. or in 50mm, min, % | Hardness, max | ||||||
HBW | HRC | ||||||||
80[550] | 116[800] | 15 | 300 | 32 |
ASTM A789 S32760 Stainless Pipe
C | Mn | P | S | Si | Ni | Cr | Mo | N | Cu |
0.05 | 1.00 | 0.030 | 0.010 | 1.00 | 6.0-8.0 | 24.0-26.0 | 3.0-4.0 | 0.20-0.30 | 0.50-1.0 |
Yield Strength min, Ksi [Mpa] | Tensile Strength, min, Ksi [Mpa] | Elongation in 2 in. or in 50mm, min, % | Hardness, max | ||||||
HBW | HRC | ||||||||
80[550] | 109[750] | 25 | 300 | - |
ASTM A789 S32900 Stainless Pipe
C | Mn | P | S | Si | Ni | Cr | Mo | N | Cu |
0.08 | 1.00 | 0.040 | 0.030 | 0.75 | 2.5-5.0 | 23.0-28.0 | 1.0-2.0 | - | - |
Yield Strength min, Ksi [Mpa] | Tensile Strength, min, Ksi [Mpa] | Elongation in 2 in. or in 50mm, min, % | Hardness, max | ||||||
HBW | HRC | ||||||||
70[480] | 90[620] | 20 | 271 | 28 |
ASTM A789 S32950 Stainless Pipe
C | Mn | P | S | Si | Ni | Cr | Mo | N | Cu |
0.030 | 2.00 | 0.035 | 0.010 | 0.60 | 3.0-5.2 | 36.0-29.0 | 1.0-2.5 | 0.15-0.35 | - |
Yield Strength min, Ksi [Mpa] | Tensile Strength, min, Ksi [Mpa] | Elongation in 2 in. or in 50mm, min, % | Hardness, max | ||||||
HBW | HRC | ||||||||
70[480] | 100[690] | 20 | 290 | 30 |
ASTM A789 S39277 Stainless Pipe
C | Mn | P | S | Si | Ni | Cr | Mo | N | Cu |
0.025 | 0.80 | 0.025 | 0.002 | 0.80 | 6.5-8.0 | 24.0-26.0 | 3.0-4.0 | 0.23-0.33 | 1.20-2.00 |
Yield Strength min, Ksi [Mpa] | Tensile Strength, min, Ksi [Mpa] | Elongation in 2 in. or in 50mm, min, % | Hardness, max | ||||||
HBW | HRC | ||||||||
90[620] | 120[825] | 25 | 290 | 30 |
ASTM A789 S32520 Stainless Pipe
C | Mn | P | S | Si | Ni | Cr | Mo | N | Cu |
0.030 | 1.50 | 0.035 | 0.020 | 0.80 | 5.5-8.0 | 23.0-25.0 | 3.0-5.0 | 0.20-0.35 | 0.50-3.00 |
Yield Strength min, Ksi [Mpa] | Tensile Strength, min, Ksi [Mpa] | Elongation in 2 in. or in 50mm, min, % | Hardness, max | ||||||
HBW | HRC | ||||||||
80[550] | 112[770] | 25 | 310 | - |
ASTM A789 S32906 Stainless Pipe
C | Mn | P | S | Si | Ni | Cr | Mo | N | Cu |
0.030 | 0.80-1.50 | 0.030 | 0.080 | 0.80 | 5.8-7.5 | 28.0-30.0 | 1.50-2.60 | 0.30-0.40 | 0.80 |
Yield Strength min, Ksi [Mpa] | Tensile Strength, min, Ksi [Mpa] | Elongation in 2 in. or in 50mm, min, % | Hardness, max | ||||||
HBW | HRC | ||||||||
94[650] | 116[8] | 25 | 300 | 32 |